Plastalloy Physical Properties
Aging
| Compressive Yield Strength after 7 days at 200 F, psi |
4870 |
| Moldulus of Elasticity in Compression after 7 days at 200 F, psi |
46500 |
| Modulus of Elasticity in Tension 600 hr. Salt Spray, psi |
50000 |
| Ultimate Tensile Strength after 600 hr. Salt Spray, psi |
800 |
| Ultimate Tensile Strength after 1000 hr. (Weather-O-Meter), psi |
750 |
| Ultimate Elongation after 1000 hr. (Weather-O-Meter), % |
4.6 |
| Ultimate Elongation after 600 hr. Salt Spray, % |
8.2 |
| Modulus of Elasticity in Tension after 1000 hr. (Weather-O-Meter), psi |
166000 |
Mechanical
| Durometer Hardness Shore D |
35-60 |
| Izod Impact Strength, ft-lb/in. of Notch |
1.6 |
| Ultimate Tensile Strength, psi |
600 |
| Elongation at Break, % |
3 |
| Modulus of Elasticity in Tensionn, psi |
67000 |
| Ultimate Shear Strength, psi |
1620 |
| Compression Yield Strength |
3700 |
| Modulus of Elasticity in Compression, psi |
30100 |
Electrical
| Volume Resistivity (X1010) ohm-cm |
3.5 |
| Insulation Resistance (X106) ohm |
6.95 |
| Arc Resistance, sec. |
100 |
Thermal
| Heat Distortian Temp., 264 psi., F |
115 |
| Heat Distortian Temp., 66psi., F |
170 |
| Thermal Conductivity Btu / hr. / F / in. |
4.3 |
| Coefficient of Cubical Thermal Expansion X10-5 per F |
5.2 |
| Maximum Operating Temp., F |
300 |
| Coefficient of Linear Thermal Expansion X10-5 per F |
2.59 |
|
|
|
|